Polyethylene fibres of various draw ratio up to 30:1 have been crosslinked by electron beam irradiation in acetylene. The gel fraction increased with dose and showed a significant increase with draw ratio above 10:1. The fibres were examined by differential scanning calorimetry, dynamic mechanical analysis and X-ray crystallography. Fibres of higher draw ratio showed a sharper decrease in melting temperature with dose, ascribed to crosslinking at fold surfaces and greater chain scission, due to higher crystallinity. The main finding was that crosslinking increases the -50°C dynamic storage modulus at intermediate draw ratio (10:1), but not at low or high draw ratio. The results were interpreted via the random intercrystalline bridge model, which suggests that at 10:1, there is good interlamellar contact but very few intercrystalline bridges. The crosslinking can therefore link together adjacent lamellae at fold surfaces and hence provide crystalline continuity, increasing the modulus.

Детальніше...  

Solid polyamide-6/CaCl 2 polymer complexes with values of the salt/polymer repeat unit molar ratio (z) as high as 40% were prepared by a new method involving room-temperature extrusion of a blend of polymer and salt powders in the presence of small amounts of methanol, followed by solvent elimination and drying. Complexation between polymer amide groups and salt ions was investigated by infra-red spectroscopy, wide-angle X-ray scattering and differential thermal analysis. Complexes were shown to absorb water more readily and to a greater extent than the parent polymer. The plasticizing effect of water on this type of material was demonstrated by dynamic mechanical measurements.

Детальніше...  

a-Organotin alcohols and quaternary ammonium salts, when used jointly, present a very high activity for the trimerization of aromatic isocyanates. If used separately, no catalytic activity is observed

Детальніше...  

The refractive indices and densities of recently synthesized poly(thiocarbonate)s and poly(dithiocarbonate)s were measured, and were used to determine the group contributions of thiocarbonate (-O-CO-S-) and dithiocarbonate (-S-CO S-) groups to the molar refraction. The high refractive indices observed make these polymers, particularly the poly(dithiocarbonate)s, potentially interesting for optical applications (i.e. lenses and optical fibres).

Детальніше...  

The distribution of the co-units between the crystalline and amorphous phases in a series of five ethylene-l-butene copolymers has been studied by means of X-ray diffraction measurements in the framework of Balta-Calleja's model for the crystalline insertion of structural chain defects. This model assumes that the side groups are accommodated at interstitial positions within the crystalline phase owing to 2gl kinks of the main chain. The defect concentration in the crystalline phase of solution-crystallized samples is shown to be fairly insensitive to the solution concentration. Besides, the determination of the crystalline and amorphous chain defect concentrations in the melt-crystallized copolymers, together with the study of their melting behaviour, allowed us to draw the ethylene-rich side of the poly(ethylene-co-butene) phase diagram for normal pressure crystallization. The self-consistency of the present data and the favourable comparison with recent 13 C n.m.r, spectroscopic measurements give support to the interstitial kink model. In addition, our results clearly indicate that the solubility of the butene co-units in the crystal is governed by thermodynamic equilibrium.

Детальніше...  

Heat capacities of alternating, statistical and diblock copolymers of styrene and methyl methacrylate were measured with a differential scanning calorimeter from 200 to 450 K to examine the additivity of heat capacity. In both solid and liquid regions, the heat capacity was found to be additive, in most cases within _ 2% error irrespective of sequence length distribution. The glass transition temperatures, determined from enthalpy-temperature plots, depended on sequence length distribution as well as composition. This behaviour, although theoretically expected, was found to be complicated by another factor, tacticity

Детальніше...  

This work reports the development of nitrodisplacement reactions between catechol and nitrophthalodinitriles, thus providing a bis(ether anhydride) and high-molecular-weight, thermally stable poly(ether imide)s with ortho-linked units. These polymers are far more soluble and more readily processable than corresponding polymers with para- and meta-linked diol units.

Детальніше...  

Scanning electron microscope (SEM) images have been obtained of polystyrene grafted onto mica with ultrahigh specific surface area and sputter coated with 1 nm tungsten. These images show separated 'droplets' of a mean diameter of ca. 30 nm. Comparison of the number and size of these droplets with other experimental data such as weight fraction grafted polymer and molecular weight of the grafted polymer suggests that the droplets observed are nanophases consisting of individual polymer molecules. The droplets have also been imaged using atomic-force microscopy (AFM). The diameters appear larger with AFM than with SEM. This appears to be an artifact of the AFM resulting from the nano-scale needle tip dimensions

Детальніше...  

Dielectric permittivity and loss have been measured over the frequency range 10-2 Hz-10 kHz between 100 K and 350 K for samples of two mesomorphic side-chain poly(vinyl ether)s, poly(4-(11-(vinyloxy)undecyloxy)- 4-ethoxyphenylbenzoate) (P-EtO) and poly(4-(11-(vinyloxy)undecyloxy)-4-cyanophenylbenzoate) (P-CN) of different degree of mesogen group orientation. X-ray scattering showed that P-EtO was in a semicrystalline state below 345 K, whereas P-CN displayed a tilted smectic structure at temperatures lower than 315 K. Four relaxation transitions were found in P-EtO: ~, the glass-rubber transition occurring at 290-300 K, and three subglass processes referred to as/~, 7 and 6. P-CN exhibited only three dielectric processes, ~,/~ and 7. The low temperature process, 6, was absent in P-CN and could be assigned to torsion about the pendent phenyl-carbon-ether-oxygen bond. Subglass processes/~ and 7 exhibited an Arrhenius temperature dependence with activation energies of 60-105 and 32+ 2 kJmol-1, respectively. The activation energy of the 7 process was insensitive to morphology and it was assigned to local motions in the spacer group. The activation energy of the/~ process varied considerably among the studied polymers with higher values for the highly ordered P-EtO than for P-CN. It is suggested that the/~ process leads to reorientation of the carboxylic group in the phenyl benzoate moiety.

Детальніше...  

3-Methoxy-4-(2-hydroxy-3-methacryloloxypropoxy)benzaldehyde (MHMPB) was prepared by reacting vanilline with glycidyl methacrylate in the presence of tetrabutylammonium bromide. Copolymers of MHMPB and methyl methacrylate (MMA) were prepared in dimethylformamide using azobisisobutyronitrile as the initiator. The compositions of the copolymers were determined by tH n.m.r, analysis and reactivity ratios were calculated using the Kelen-Tiid6s linear differential equation.

Детальніше...  

Корисні статті

Хімічне машинобудування

Хімічне машинобудування багатопрофільна галузь машинобудування, що поєднує в собі природні та експериментальні науки (наприклад, фізика і хімія), разом з науками про життя (наприклад, біологія, мікробіологія та біохімія). Математику та економіку вокористовують для розробки, перетворення, транспортування, управління виробничими процесами, які перетворюють сировину в цінні продукти.

Полімерні матеріали

Полімер це велика молекула, або макромолекула, котра складається з багатьох субодиниць. Через їх широкий спектр властивостей, синтетичні і природні полімери відіграють найважливішу і всюдисущу роль в повсякденному житті. Полімери в діапазоні від знайомих синтетичних пластмас, таких як полістирол природний біополімер, таких як ДНК і білки, які є основоположними для біологічної структури і функцій. Полімери, як природні і синтетичні, створюються за допомогою полімеризації багатьох малих молекул, відомих як мономери.

Хто такий інженер

Інженер - професія нелегка, але одночасно з цим дуже цікава і захоплююча. Адже інженер це людина, у якого народжуються в голові нові ідеї і тому він здатний винаходити.

У багатьох виникає питання: хто такі інженери? Інженер (франц. Ingénieur) - фахівець з вищою технічною освітою. Спочатку інженерами називали людей, які керували військовими машинами. Поняття громадський інженер з'явилося в XVI столітті в Голландії, застосовано до сфери будівництва мостів і доріг, потім інженери з'явилися в Англії, а потім в інших країнах.

Інженер-конструктор

Хто такий інженер-конструктор? Даним питанням задаються багато людей, які бажають пов'язати своє життя з цією професією. Варто відзначити, що ця професія однією з найбільш високооплачуваних на сучасному ринку праці, яка характеризується високим попитом з боку роботодавців. Інженер-конструктор машинобудування повинен володіти аналітичним складом розуму, підвищеною уважністю до деталей і відповідальним підходом до роботи. Дана діяльність пов'язана з прорахунками і різноманітним обладнанням. Першокласний інженер-конструктор механік володіє також такими рисами характеру, як раціональність і ерудованість. Важливу роль відіграє стресостійкість, адже робочий процес є досить трудомістким і при потребі замовника вимагає готовності швидко вносити зміни в готові креслення.

Інженер-механік

Інженер-механік (від лат. Ingenium – талант, обдарованість, і mēchanicus – механік) – це технічний чи технологічний фахівець з вищою освітою, який застосовує отримані знання для конструювання, проектування, моделювання та експлуатації машин, апаратів та технічного обладнання в різних галузях сільського господарства та технічного виробництва. Першими з інженерів були саме механіки; вони розробляли і збирали різноманітні машини і механізми, в яких використовували принципи і закони механіки.