We have investigated the influence of strain rate during hot-drawing of poly(ethylene terephthalate) on the kinetics of overall crystallization and of crystal growth normal to the 010 and 100 planes. Drawing was at 90°C and at various strain rates between 0.01 s- 1 and 2.1 s- 1. We found that changing strain rate simply shifts the crystallization rate curves along the log time axis, that the shift factor and the strain rate are related by a power law, and that the value of the exponent reflects the relative influence of two effects of molecular mobility : relaxation of orientation and enhancement of crystallization. The relative importance of these two effects was found to be different in different crystallographic growth directions : normal to the 100 planes, they almost exactly compensate each other; normal to the 010 planes, the relaxation effect dominates. By defining an 'equivalent time' for crystallization, degree of crystallinity at any strain rate can be predicted from knowledge of either draw time or draw ratio. A similar treatment permits prediction of crystallite size.
Phase diagrams were constructed experimentally for mixtures of a polystyrene-block-polyisoprene-blockpolystyrene (SIS) copolymer and a homopolymer polystyrene. For the study, two SIS triblock copolymers having spherical and cylindrical microdomain structures, respectively, and a series of homopolymer polystyrenes were synthesized via anionic polymerization. In constructing phase diagrams, we combined the results of dynamic viscoelastic measurement (i.e. logarithmic plots of dynamic storage modulus versus dynamic loss modulus), which allowed us to determine the boundary between the mesophase and homogeneous phase, and turbidity measurement, which allowed us to determine cloud point curves for liquid-liquid (macrophase) separation. Experimental results are compared with predictions made by the theory of Hong and Noolandi. We have found that predicted results are at variance with experimental results.
Values of refractive indices and birefringence of aramid fibres measured by different authors are commented on and a modified approach to the spectrophotometric method is proposed
We have investigated the suitability of the chain-intrinsic fluorescent properties of poly(ethylene terephthalate) for characterizing 'amorphous orientation' in semicrystalline films and fibres of this polymer. By developing an apparatus which permits the polarized fluorescence to be measured in the optical axis, we have eliminated possible sources of measurement error. Our results provide further evidence that the increase in fluorescence intensity at high draw ratios arises from light scattering between crystallites and not from an increase in the population of fluorescent dimers. This cause of intensity increase would have no influence on the orientation function, and one can correct for any significant depolarization due to scattered light. For hot-drawn film, the amorphous orientation data obtained from intrinsic fluorescence provide a consistent explanation of the influence of strain rate on the induction and development of crystallinity. For fibres, our intrinsic fluorescence data confirm that high speed spinning results in substantially lower amorphous orientation than spin-drawing, and that amorphous orientation goes through a maximum as a function of spinning speed. These fluorescence results are in very good qualitative agreement with data we obtained from a birefringence/X-ray method ; quantitative differences seem to arise from the choice of values for intrinsic birefringence (A ° and A° ) required in the latter method. Determination ofA?° and A ° using amorphous orientation data from the fluorescence method provides support for the argument that these values are not truly intrinsic, but are dependent on the structural state of the crystalline and amorphous regions.
The feasibility of obtaining high-solids-content latexes through miniemulsion polymerization was investigated. It was found that, for the batch terpolymerization of styrene, 2-ethylhexyl acrylate and methacrylic acid, coagulum-free 60 wt% solids-content latexes can be obtained through the miniemulsion process, whereas the maximum coagulum-free solids-content latex attainable by means of conventional emulsion polymerization was 50wt%. The effect of the type and amount of surfactant, amount of cosurfactant and sonication time on both the amount of coagulum and particle size was studied. In addition, the chemical, freeze-thaw and mechanical stabilities of the latexes were determined.
Plastic deformation in two high impact polystyrenes containing mainly small particles (average size < 1 #m) with different internal structures (core-shell, salami) has been investigated by means of transmission electron microscopy of crazed films produced using a modified procedure derived from the copper grid technique first introduced by Lauterwasser and Kramer. General evidence of the small particles being entrapped inside the crazes is presented.
The miscibility behaviour of poly(chloromethyl methacrylate) (PCMMA) and poly(2-chloroethyl methacrylate) (PCEMA) with various aliphatic polyesters was studied by differential scanning calorimetry. PCMMA and PCEMA are miscible with poly(ethylene adipate), poly(butylene adipate), poly(hexamethylene sebacate) (PHS), poly (2,2-dimethyl-l,3-propylene succinate) and poly (2,2-dimethyl- 1,3- propylene adipate). In addition, PCMMA is miscible with poly(ethylene succinate) whereas PCEMA is not. Blends of PCEMA with poly(2,2-dimethyl-l,3-propylene sebacate) exhibit upper critical solution temperature behaviour. Interaction parameters for PCMMA/PHS and PCEMA/PHS blends were evaluated from melting point depression analysis
A new method of polymerization of pyrrole in the presence of cationic photoinitiators such as iron-arene salts (q-CsHs)Fe(q-arene) under visible or ultraviolet irradiation has been described. The synthesized polypyrroles have low conductivity in the range of 10- 5 S cm- 1 and rather poor electrochemical properties. The polymerization reaction occurs only in the presence of oxygen and is inhibited by the addition of 1,10-phenanthroline. It is initiated by the Fe (In) species formed by the oxidation of Fe (u) fragments formed during the photolysis of the photoinitiators used.
We report on the mechanism of direct oxidation of 3-alkylthiophenes using ferric chloride (FeC13) as the polymerization oxidant/catalyst to produce high molecular weight poly(3-alkylthiophenes) (P3ATs), conjugated polymers that have potential as electrically and optically active polymers. This study shows that the FeCI 3 must exist in the solid state in the reaction mixture to be active as an oxidant in the polymerization of P3AT. A feasible polymerization mechanism for 3-alkylthiophene was developed on the basis of the crystal structure of FeCI 3 and quantum chemical computations of thiophene derivatives. The polymerization is hypothesized to proceed through a radical mechanism rather than a radical cation mechanism.
An aramid, prepared by the polycondensation of bis(4-aminophenyl) ether with isophthaloyl chloride, was found to render a single-phase mixture with poly(ether sulphone) (PES) by solution casting. Crystallization of the blend was studied by wide-angle X-ray diffraction, Hv light scattering, differential scanning calorimetry, Fourier-transform infra-red spectroscopy and scanning electron microscopy. The crystallization of aramid was found to be accelerated dramatically by adding PES, e.g. the crystallization rate constant of a 50/50 blend was shown to be one decade higher than that of neat aramid at around 310°C. The accelerated crystallization was ascribed to the elevation of chain mobility of aramid by blending with PES. It may be caused by the decrease of Tg via blending of a low-T~ component (PES), but this contribution was estimated to be small. The major contribution seems to be due to the partial dissociation of aramid-aramid interactions and the 'up-hill diffusion' associated with the liquid-liquid phase separation.
Корисні статті
Інженер-конструктор
Хто такий інженер-конструктор? Даним питанням задаються багато людей, які бажають пов'язати своє життя з цією професією. Варто відзначити, що ця професія однією з найбільш високооплачуваних на сучасному ринку праці, яка характеризується високим попитом з боку роботодавців. Інженер-конструктор машинобудування повинен володіти аналітичним складом розуму, підвищеною уважністю до деталей і відповідальним підходом до роботи. Дана діяльність пов'язана з прорахунками і різноманітним обладнанням. Першокласний інженер-конструктор механік володіє також такими рисами характеру, як раціональність і ерудованість. Важливу роль відіграє стресостійкість, адже робочий процес є досить трудомістким і при потребі замовника вимагає готовності швидко вносити зміни в готові креслення.
Хімічне машинобудування
Хімічне машинобудування багатопрофільна галузь машинобудування, що поєднує в собі природні та експериментальні науки (наприклад, фізика і хімія), разом з науками про життя (наприклад, біологія, мікробіологія та біохімія). Математику та економіку вокористовують для розробки, перетворення, транспортування, управління виробничими процесами, які перетворюють сировину в цінні продукти.
Рейтинг вищих навчальних закладів
На даний час в світі існує маса університетів з дуже великою кількістю кваліфікацій, спеціальностей та спеціалізацій. Одні з них більш престижні університети, інші менш.
Рейтинг вищих навчальних закладів переписується щорічно, в зв'язку з тим, що всі прагнуть стати краще в освіті, вдосконалитися в технологіях і підвищити свій рівень акредитації. Рейтинг навчальних закладів варіюється в залежності від предметної області, це природничі науки і математика, техніка/технологія і інформатика, життя і сільськогосподарська наука, клінічна медицина і фармація, соціальні науки.
Як стати інженером?
Кожна людина в процесі свідомого життя стикається з проблемою вибору професії. Найбільш актуальною ця проблема є для учнів старших класів – випускників, які добровільно або примусово здають шкільні іспити та зовнішнє незалежне оцінювання, за результатами чого приймають участь в конкурсному відборі на навчання у ВНЗ. Щоб обрана професія не стала важким випробовуванням, потрібно ще у шкільні роки зважити всі «за» і «проти», оцінити свої здібності, схильності, можливості.
Комп'ютер для інженера
У сучасному світі комп'ютери дуже поширені. Складно уявити людину, не знайому з цим поняттям. Багато професій зобов'язані своїм виникненням саме комп'ютеру, вони б просто не з'явилися без створення електронно-обчислювальної техніки.
І хоча відносно недавно, на початку XX століття, комп'ютери були розкішшю і використовувалися лише для самих складних розрахунків, у наш час комп'ютери та комп'ютерна техніка дуже глибоко інтегрувалися у наше життя. Сучасне людство залежить від комп'ютерів, що викликає подиву, якщо розглянути, коли і в яких випадках вони використовуються.