The adsorption of polyelectrolytes onto plasma-pretreated poly(tetrafluoroethylene) (PTFE) surfaces is reported as a method for fluoropolymer surface modification. PTFE was treated in oxygen or ammonia plasmas in order to introduce oxygen-containing and nitrogencontaining groups, respectively, which increase the surface free energy and make possible the adsorption of polyelectrolytes via electrostatic interactions. We investigated the adsorption of poly(diallyldimethylammonium chloride) and poly(sodium styrenesulfonate) on the plasmapretreated PTFE. The modification effects were evaluated by means of contact angle and streaming potential measurements.
The cellulose solutions in N-methyl-morpholine-N-oxide (MMNO)/H2O were prepared. The cellulose concentration was varied from 5 to 25 wt.%. The mole ratio of water to MMNO was fixed at 0.8 and propyl gallate (,1 wt.%) was added as an antioxidant. To observe the anisotropic phase formation, polarized light microscopy, DSC, dynamic rotational rheometry and capillary rheometry experiments were performed. Polarized light micrographs revealed anisotropy for the cellulose solutions of 20 wt.% and higher concentrations. The anisotropy become clearer when sheared. It was difficult to detect the isotropic transition temperature and concentration from DSC and dynamic viscosity. In capillary rheometry measurements, however, both viscosity drop at the anisotropic to isotropic transition concentration and flow activation energy change at the transition temperature were observed. The phase transition temperature and concentration were 958C–1008C and about 23 wt.%, respectively. Time–temperature superposition principle was applied successfully to the solutions below 20 wt.% concentration but failed for the solutions above 20 wt.% concentration. The largest deviation from superposition was found at 23 wt.% solution which was the critical concentration.
A modified Nylon 6 formulation, developed originally for reaction injection moulding, has been used to freeform small parts. Liquid monomer is deposited as a fine stream from computer-controlled writing head and polymerizes on a heated plate as the part is built up. This is the first example of rapid prototyping of a linear polymer by direct polymerization. Nylon was chosen for this work because it attains good mechanical properties at relatively low molecular weights, so limiting the extent of chain propagation necessary. Freeformed bars were made with a strength of 75 MPa and tensile modulus of 2.3 GPa.
This article describes a study on flame retardancy conducted on a dual cure thermosetting system consisting of an epoxy resin, blended with an unsaturated polyester. Neat resin panels and glass-fibre reinforced composites were prepared utilising several structurally different flame-retardant (FR) additives. These materials were tested in order to determine the Limiting Oxygen Index (LOI), which is a measure of the fire performance properties of a given material. Particular attention was paid to the FR properties of compounds, which are free of halogen such as bromine, in the absence of antimony oxide. These compounds are based on phosphorous containing molecules.
The crystallizable component poly(ethylene oxide) (PEO) displays liquid–liquid phase separation in blends with the rigid amorphous aromatic polyamide, Aramide 34I. The crystallization, melting behavior and the semi-crystalline morphology after crystallization from the miscible state, are investigated. It is found that the amorphous component, Aramide 34I, has a pronounced effect on the crystallization behavior of PEO; PEO can only be crystallized up to 35 wt.% of Aramide 34I. A complex melting behavior of PEO with secondary crystallization and recrystallization, in which the amorphous component segregates interlamellarly during crystallization, is described. A lamellar insertion model is proposed for the location of the secondary lamellae.
Thermal, mechanical, dynamical mechanical and morphological investigations are reported of two series of blends of poly(ethylene terephthalate) (PET) with two nematogenic random polymers synthesized in our laboratory. The nucleant effect of low amounts of the liquidcrystalline component (LCP) is evidenced by thermal analysis for both polymers. At higher LCP contents this effect disappears but a new influence on the melting enthalpy of PET emerges, although at contents of the random polymer that are remarkably different for the two series of blends. The coupling of mechanical tests with a morphological study allowed elucidation of the reinforcing mechanism of one of the nematogenic polymers and the explanation of the discontinuity in the rise of Young’s modulus shown by these blends.
We utilized the light scattering from the anisotropy of turbidity (LSAT) method and evaluated, for the first time, the three elastic constants of dilute solutions of polystyrene (PS) in 4-pentyl-4 0 -cyanobiphenyl (5CB) nematic solvent. Within the solubility range of this system (less than 5%), the elastic constants of splay (K1), twist (K2), and bend (K3) of PS/5CB solution were determined as a function of concentration and molecular weight of PS solute. The experimental results showed a systematic diversion of the elastic constants and, in particular, a large increase in K1 with increasing concentration and molecular weight of PS. The results are in agreement with the predicted theoretical models and other experimental data. Determination of Ki in polymer/nematic solutions with LSAT is a promising experimental approach to study the macromolecular chain structure of flexible, semi-flexible and rigid-rod polymers in anisotropic regimes.
An evaluation was made of pins of poly(lactic acid), an absorbable polymer, produced both with very little crystallinity (PLLA-A) and with extensive crystallinity (PLLA-C). These polymer pins were submitted to in vitro tests to evaluate the effects of degradation on mechanical, thermal, and structural properties, as well as molar mass variation. The pins were molded and immersed in a phosphate buffer solution (pH 7.4) for 6 months. The results showed pins with greater crystallinity lost their mechanical properties more quickly, although an increase in the degree of crystallinity for both types of pins was observed over time. Structural analyses showed both superficial and internal erosion after two months of degradation. The greater retention of mechanical properties of the less-crystalline PLLA-A should prove useful in the production of implants where the stimulation of osteosynthesis is desired.
Polyester-based polyurethane elastomers with alkyl side groups were prepared from poly(adipate) glycols which involved 2,4-diethylpentamethylenediol or 3-methyl-pentamethylene diol as a novel glycol component and 1,5-pentamethylenediol. Segmented and allophanatecrosslinked polyurethane elastomers were prepared from these polymer glycols, 4,4⬘-diphenylmethane diisocyanate and 1,4-butanediol by a prepolymer method. Mechanical properties, dynamic viscoelastic properties, glass transition temperature (T g), and thermal hydrolytic stability were measured. The properties of the polyurethane elastomers with alkyl side groups have good mechanical properties comparable to those of general purpose polyester urethanes. Novel polyester polyurethane elastomers with alkyl side groups had improved hydrothermal stability due to steric hindrance from hydrolysis of ester groups.
The conventional emulsion and miniemulsion polymerization of vinyl acetate in a continuous stirred tank reactor (CSTR) were studied in an attempt to demonstrate the feasibility of miniemulsion polymerization as a strategy to eliminate the oscillatory behaviour of CSTR reactors, even in very unfavourable conditions. Reactions were carried out under a wide range of operating conditions. No oscillations in the time evolution of the conversion and particle number were observed in any of the miniemulsion polymerizations, while the opposite was found in most of the conventional emulsion polymerizations. Different dependencies of the emulsifier and initiator concentrations on the reaction rate and particle number were obtained for both emulsion and miniemulsion polymerizations, as a consequence of the different nucleation mechanisms. Further, almost the same average molecular weight was obtained for the emulsions and miniemulsions carried out under similar experimental conditions.
Корисні статті
ВНЗ України
Вища освіта є невід'ємним елементом перспективного кар'єрного росту, тому перед кожним абітурієнтом виникає проблема, в які інститути подавати документи. Варто відзначити, що в Україні існує велика кількість вузів. Всі навчальні заклади поділяються на державні та приватні, пропонуючи різноманітні освітні програми по різних профілів. Щоб пошук інститутів дав задовільні результати, слід визначитися з найбільш прийнятними спеціальностями. Також підбір університету передбачає вибір підходящої форми навчання, наявність високої акредитації у вузу і рівень його престижності.
Види та функції сучасної упаковки
Різноманітна упаковка щільно увішла у життя кожної людини. На полицях магазинів, в інтер'єрах помешкань можна побачити десятки пляшочок, коробок, аерозольних болончиків. Термін існування упаковки в нашому житті може продовжуватися від кількох хвилин до кількох років. Що ж таке сучасна упаковка? Чому вона займає стільки місця в нашому житті?
Комп'ютер для інженера
У сучасному світі комп'ютери дуже поширені. Складно уявити людину, не знайому з цим поняттям. Багато професій зобов'язані своїм виникненням саме комп'ютеру, вони б просто не з'явилися без створення електронно-обчислювальної техніки.
І хоча відносно недавно, на початку XX століття, комп'ютери були розкішшю і використовувалися лише для самих складних розрахунків, у наш час комп'ютери та комп'ютерна техніка дуже глибоко інтегрувалися у наше життя. Сучасне людство залежить від комп'ютерів, що викликає подиву, якщо розглянути, коли і в яких випадках вони використовуються.
Інженер-конструктор
Хто такий інженер-конструктор? Даним питанням задаються багато людей, які бажають пов'язати своє життя з цією професією. Варто відзначити, що ця професія однією з найбільш високооплачуваних на сучасному ринку праці, яка характеризується високим попитом з боку роботодавців. Інженер-конструктор машинобудування повинен володіти аналітичним складом розуму, підвищеною уважністю до деталей і відповідальним підходом до роботи. Дана діяльність пов'язана з прорахунками і різноманітним обладнанням. Першокласний інженер-конструктор механік володіє також такими рисами характеру, як раціональність і ерудованість. Важливу роль відіграє стресостійкість, адже робочий процес є досить трудомістким і при потребі замовника вимагає готовності швидко вносити зміни в готові креслення.
Інженер-машинобудівник
Ні для кого не секрет, що при сучасних умовах життя, темпах розвитку промисловості, безперервній автоматизації та оптимізації роботи механізмів та виробничих процесів, великою популярністю та попитом на ринку праці користується професія інженера, особливо інженера-машинобудівника.
Щоб відповісти на питання «Хто такий інженер-машинобудівник?», необхідно розуміти , що несе в собі кожне з цих слів окремо. Інженер – це людина, яка отримала освіту з визначеного фаху. Інженер – це творець техніки. Інженер – це особа, що професійно займається інженерією, тобто на основі поєднання прикладних наукових знань, математики та винахідництва знаходить нові рішення технічних проблем. Тобто, виходячи з цих загальновживаних визначень слова «інженер» зрозуміло, що цій професії може присвятити себе лише людина з неабиякими здібностями, які ґрунтуються на знанні точних наук, логічному мисленні, невичерпному терпінні і постійному бажанні вдосконалювати світ інженерії. Від латини ingenium — здатність, винахідливість, що є свідченням того, що інженером перш за все є людина-думаюча, яка знаходиться в безперервному пошуку відповідей на складні технічні завдання.