The conductivity behaviour of the system poly(ethylene glycol) (PEG)-sodium iodide (NaI) has been studied by varying the ratio of the metal salt and PEG. A maximum conductivity of 10- 6 f~- 1 cm- 1 is observed for PEG~oNaI samples at 25°C. The conductivity increases by two orders of magnitude as compared to pure PEG and has been shown to be due to ionic carriers. This behaviour is similar to that exhibited by the analogous poly(ethylene oxide) system
Data of the copolymerization of styrene with benzonitrile are presented. The effect of reactivity of monomers, catalyst nature, temperature and process duration on the composition and molecular weight of the formed polymers are discussed. The polymerization mechanism is suggested. Copolymers of different composition were used for synthesis of soluble polyelectrolytes. The conditions of their formation and principal physico-chemical characteristics were studied. The fields of application are discussed.
Based on the results of integrated analysis given in parts 1 and 2, a kinetics-gelation mechanism of styrene (ST)/unsaturated polyester (UPE) resins is proposed. The curing process can be divided into five stages: induction, microgel formation, transition with or without phase separation, macrogelation and post-gelation. A summary of the experimental results at different stages of ST/UPE resins with ST/UPE molar ratios of 2 and 4 at 40°C is given. The kinetics-gelation mechanism based on the concept of microstructure formation is then discussed
The photo-Fries reaction of aryl esters provides a mechanism for the stimulation of a selective photoinduced structural rearrangement. We demonstrate that, in a side-chain liquid-crystal polymer containing 20% 4-methoxyphenyl cinnamate and 80% 4-cyanophenyl benzoate mesogens, photoinduced phase depressions may be achieved by selective irradiation of the cinnamate esters. When only the photo-Fries process is activated, by irradiation in dilute solution, subsequent phase depressions as high as 60-70°C are observed. In the liquid-crystalline state, other photoprocesses, including crosslinking, tend to predominate over the photo-Fries reaction and inhibit large-scale rearrangement, and hence rather limited phase transition shifts are observed
Inherently conducting polymers have been used as microwave absorbers to weld thermoplastic materials. The welding takes place in 2-120 s with lap shear strengths as high as 19.0+2.0 N mm -2. The method can be applied to any thermoplastics.
The imidization behaviour of the isomeric poly(amic ethyl ester) (PAE) precursor molecules of the polyimide pyromellitic dianhydride oxydianiline was followed using forward recoil spectrometry. The degree of imidization after 1 h at various temperatures was found to depend strongly on the spin-casting solvent. Films cast from dimethyl sulfoxide (DMSO) showed an imide fraction, f, which was independent of depth and of isomeric precursor (i.e. whether the precursor was para-PAE, meta-PAE or a random mixture of meta and para (mixed-PAE).) In films spun cast from N-methylpyrrolidone (NMP), however, fs for the para- and mixed-PAE were larger than that for the meta-PAE. In addition the fs for the para-PAE and mixed-PAE were found to be greater for films cast from NMP than from DMSO for any given thermal treatment. For the meta-PAE, f was independent of the casting solvent. Over an imidization temperature range of 180-280°Cfwas found to vary with depth, being lower than the bulk value over the first 3000/~ from the film surface. These observations appear to be related to a retention of the NMP with f being larger where NMP is retained.
The morphology of isothermally crystallized samples of two copolymers of poly (ether ketone) (PEK) has been examined using X-ray diffraction and differential scanning calorimetry (d.s.c.) techniques and compared with that of the PEK homopolymer. One copolymer contains 15 mol% of aryl ether sulfone (ES) units, whose homopolymer, 'PES', does not normally crystallize. The second copolymer contains 33 mol% of ether biphenyl ether ketone (EDEK) units, whose homopolymer, 'PEDEK', does crystallize. The crystal structure of PEDEK has a close resemblance to that of poly(ether ether ketone) (PEEK) and has a unit cell with a = 7.72 A, b = 5.94 A and c = 37.5 A. Both the ES and EDEK copolymers have a depressed Tm and reduced crystallinity. D.s.c. scans of both copolymers and PEK show a small low-temperature endotherm about 20°C above the crystallization temperature, together with an almost invariant final endotherm. At lower crystallization temperatures, the EDEK copolymer can show an additional middle endotherm at 315°C, which is associated with the melting of an EDEK lattice, which is then replaced by a higher-melting EK lattice. The formation of the EDEK structures is difficult to reproduce and indicates a competition in the kinetics of nucleation of the crystals. The ES copolymer crystallizes over the middle of the crystallization range with an EK cell consistent with exclusion of ES units. However, in the lower- and higher-temperature regions there is a change in the diffraction, indicating an association of the ES units with the crystals. At lower temperatures the ES copolymer can also show a middle d.s.c, peak
We propose a simple four-particle interaction model to describe the phase transition in the poly(vinylidene fluoride trifluoroethylene) [P(VDF-TrFE)] system. The mean field treatment of this model displays the main qualitative behaviour of the copolymer by predicting a tricritical point for an equimolar VDF-TrFE sample and the thermal evolution of the order parameter for the different sample compositions
Benzo[18]crown-6 was incorporated into pendent groups of poly(N-isopropylacrylamide) to obtain chemical-responsive polymer systems. The aqueous solution of the polymer containing l 1.6 mol% pendent benzo[18]crown-6 groups underwent a phase transition from the phase-separated to the homogeneous state at 32°C by the addition of K + and Na +. The threshold ion concentration to induce the phase transition depended on the kind of metal ion. A very small amount of K + was sufficient to induce the transition, while 6.0 x 10 2M Na + was required. At 37°C only K + could induce the phase transition.
The polymerization of bisphenol-A epoxy resin mixed with a curing agent (methyltetrahydrophthalic anhydride) was followed from the liquid to the solid state using the positron annihilation lifetime (PAL) technique at several curing temperatures. With the commencement of polymerization, the intensity, I3, of ortho-positronium started to increase, followed by a sharp decrease of its lifetime, T3. When the curing temperature was raised further, 13 increased to a large value, indicating further propagation of the polymer networks. When the polymerization was terminated, T 3 reached the smallest value and 13 reached a large saturation value. PAL is a powerful technique for studying microscopic structural changes and state transitions of polymers.
Корисні статті
Хімічне машинобудування
Хімічне машинобудування багатопрофільна галузь машинобудування, що поєднує в собі природні та експериментальні науки (наприклад, фізика і хімія), разом з науками про життя (наприклад, біологія, мікробіологія та біохімія). Математику та економіку вокористовують для розробки, перетворення, транспортування, управління виробничими процесами, які перетворюють сировину в цінні продукти.
Інженер-машинобудівник
Ні для кого не секрет, що при сучасних умовах життя, темпах розвитку промисловості, безперервній автоматизації та оптимізації роботи механізмів та виробничих процесів, великою популярністю та попитом на ринку праці користується професія інженера, особливо інженера-машинобудівника.
Щоб відповісти на питання «Хто такий інженер-машинобудівник?», необхідно розуміти , що несе в собі кожне з цих слів окремо. Інженер – це людина, яка отримала освіту з визначеного фаху. Інженер – це творець техніки. Інженер – це особа, що професійно займається інженерією, тобто на основі поєднання прикладних наукових знань, математики та винахідництва знаходить нові рішення технічних проблем. Тобто, виходячи з цих загальновживаних визначень слова «інженер» зрозуміло, що цій професії може присвятити себе лише людина з неабиякими здібностями, які ґрунтуються на знанні точних наук, логічному мисленні, невичерпному терпінні і постійному бажанні вдосконалювати світ інженерії. Від латини ingenium — здатність, винахідливість, що є свідченням того, що інженером перш за все є людина-думаюча, яка знаходиться в безперервному пошуку відповідей на складні технічні завдання.
ВНЗ України
Вища освіта є невід'ємним елементом перспективного кар'єрного росту, тому перед кожним абітурієнтом виникає проблема, в які інститути подавати документи. Варто відзначити, що в Україні існує велика кількість вузів. Всі навчальні заклади поділяються на державні та приватні, пропонуючи різноманітні освітні програми по різних профілів. Щоб пошук інститутів дав задовільні результати, слід визначитися з найбільш прийнятними спеціальностями. Також підбір університету передбачає вибір підходящої форми навчання, наявність високої акредитації у вузу і рівень його престижності.
Як стати інженером?
Кожна людина в процесі свідомого життя стикається з проблемою вибору професії. Найбільш актуальною ця проблема є для учнів старших класів – випускників, які добровільно або примусово здають шкільні іспити та зовнішнє незалежне оцінювання, за результатами чого приймають участь в конкурсному відборі на навчання у ВНЗ. Щоб обрана професія не стала важким випробовуванням, потрібно ще у шкільні роки зважити всі «за» і «проти», оцінити свої здібності, схильності, можливості.
Види та функції сучасної упаковки
Різноманітна упаковка щільно увішла у життя кожної людини. На полицях магазинів, в інтер'єрах помешкань можна побачити десятки пляшочок, коробок, аерозольних болончиків. Термін існування упаковки в нашому житті може продовжуватися від кількох хвилин до кількох років. Що ж таке сучасна упаковка? Чому вона займає стільки місця в нашому житті?