The crystallization behaviour of a microphase-separated diblock copolymer, e-caprolactone-block-butadiene (PCL-b-PB), was observed by small-angle X-ray scattering employing synchrotron radiation. The Avrami analysis at the early stage of crystallization did not show any significant difference between PCL-b-PB and a poly(e-caprolactone) homopolymer (PCL), suggesting that the initially existing microphase structure does not affect the early stage of crystallization. In the late stage, the crystallization of PCL-b-PB was significantly retarded compared to the case of PCL, and the rate was dependent on the microphase structure and/or molecular characteristics of the copolymer

Детальніше...  

Highly processable heat-resistant resins containing o-phenylene rings have been prepared with high molecular weight from the reaction of simple aromatic dianhydrides with aromatic diamines containing preformed bisbenzoheterocyclic groups connected by an o-phenylene ring. Thus, 2,2'-o-phenylene-bis(5- aminobenzoxazole) was polycondensed with 3,3'4,4'-benzophenone dianhydride to yield a polyamic acid precursor, which was converted to an ordered benzoxazole-imide copolymer via cyclodehydration. Polymers can be prepared from diamines that are structural isomers, e.g. the amino groups can be in the 6-position instead of the 5-position. Additionally, polymers have been prepared from diamines, e.g. 2,2'-o-bis(6- aminobenzothiazole), having structurally similar heterocyclic units such as benzothiazole in place of benzoxazole rings. The preparation of the dinitro precursors to the bisbenzoheterocyclic diamines and their reduction is described along with nuclear magnetic resonance data. Polymers were characterized by differential scanning calorimetry, thermogravimetric analysis and inherent viscosity measurements of the polyamic acid precursors

Детальніше...  

The possibility of a low-temperature glass transition is proposed for two poly(amino acid)s: poly(L-methionine) and poly(L-serine). The suggestion is based on deviations of the experimental heat capacity from values calculated from the vibrational spectrum. The discrepancy consists in an increase of the heat capacity over a wide temperature range (260-400 K) to values more typical of liquids. Qualitative experiments are performed that show the rubbery nature of the samples above room temperature and brittleness below. The broadness of the proposed glass transition may be caused by the presence of some low level of crystallinity. It is speculated that the motion begins in the side groups around room temperature and causes a gradual devitrification of the whole molecule at higher temperatures.

Детальніше...  

The solubility of many alkali metal salts shows negative temperature dependence in poly(ethylene oxide) (PEO) oligomer. When a PEO oligomer solution containing salt is heated, salt crystals are phase separated. This unusual phenomenon was analysed systematically for a variety of inorganic salts. These salts were shown to have relatively high lattice energy and are known to form no complex with PEO.

Детальніше...  

Toughening procedures, processing optimization and performance evaluation of bismaleimide (BMI)-carbon fibre composites are reported. The BMI matrix was 4,4'-bismaleimidodiphenylmethane( BM PM)/O,O'-diallyl bisphenol A (DABPA). Toughening procedures involved (i) characterization and optimization of the BMI cure reactions to produce 'defect-free', fully cured crosslinked networks, and (ii) incorporation of viscoelastic toughening poly(ether imide) (PEI) particulates and film interleaves and crack deflector Kevlar 49 whiskers into the BMI-carbon fibre composites. Optimization of composite processing conditions is reported. The effects of toughening procedures on composite performance in terms of G k toughness, impact penetration, compression after impact and open hole compression as a function of temperature are discussed. The conflicting requirements of these performance tests upon desirable polymer matrix properties are critically discussed.

Детальніше...  

Crystallization of synthetic trans-l,4-polyisoprene (TPI) at -20°C in hexane and amylacetate solutions gave chain-folded s-type crystals with 53% and 57% crystallinity, respectively. Selective ozonolysis degradation of the isoprene units in the surface folds associated with high-resolution g.p.c, measurement was used to determine the crystalline stem length, stem length distribution and fold surface structure of the ~-TPI crystals. As ozone uptake increased, the isoprene units of the main fraction of oligomer products were found to decrease from 13, reaching a constant value at 11 for hexane and 12 for amylacetate. The polydispersity of the oligomer fractions was found to be in the range of 1.01-1.02. These findings suggested that the chain fold structure might be tight folding with slightly irregular folds, with a stem length of 11 monomers and a dispersion of 2.3 for lamellae grown from hexane, and 12 monomers with dispersion of 2.3 for those grown from amylacetate.

Детальніше...  

A series of new polyacrylates was synthesized by incorporating the hexafluoroisopropoxy unit pendant to the backbone. The fluorinated monomers were synthesized by reacting 4-fluoro(2- hydroxyhexafluoroisopropyl)benzene with acrylic or methacrylic acid chlorides. The polymers were obtained by bulk, free-radical polymerization techniques using ~,~'-azobisisobutyronitrile as initiator. The polymers had viscosities ranging from 0.15 to 1.41 dl g-1 and had good film-forming properties. Thermogravimetric analysis showed that they had thermal stability up to 370°C in N2; glass transition temperatures were in the range 64 to 119°C.

Детальніше...  

New imide-aryl ether copolymers containing a 1,2,4-triazole heterocyclic unit were prepared, and their structural, mechanical and thermal properties were studied. These copolymers contain an aryl ether 1,2,4-triazole linkage, which was incorporated into a semi-rigid backbone by the reaction of new 1,2,4-triazole diamines with 4,4'-oxydianiline (ODA) and pyromellitic dianhydride (PMDA). The 1,2,4-triazole diamines were prepared through a nucleophilic aromatic substitution reaction of 3,5-bis(4'-fluorophenyl)-4-phenyl- 1,2,4-triazole with either 3- or 4-aminophenol in the presence of K2CO3 in a polar aprotic solvent mixture to afford 3,5-bis(3'-aminophenoxyphenyl)-4-phenyl-l,2,4-triazole and 3,5-bis(4'-aminophenoxyphenyl)-4- phenyl-l,2,4-triazole, respectively. The monomers were reacted with PMDA or co-reacted with ODA and PMDA to synthesize the desired poly(amic acid)s. Films were cast and cured at 350°C to effect imidization, producing films with good mechanical properties.

Детальніше...  

A newly developed kinetic model for network structure development during emulsion crosslinking copolymerization of vinyl and divinyl monomer is used to investigate the kinetics of emulsion crosslinking copolymerization of methyl methacrylate and ethylene glycol dimethacrylate. The agreement of predicted with measured development of crosslinking density and that of monomer concentration in the polymer particles is found to be satisfactory. It is shown that the crosslinking density is fairly high even from very early stages of polymerization and that the produced polymeric networks tend to be highly heterogeneous. The kinetics of crosslinking and resulting network structure are essentially different from those for polymerizations in homogeneous media such as bulk and solution polymerization.

Детальніше...  

The crystal structure and morphology has been examined in a series of 4-hydroxybenzoic acid (HBA) and 2-hydroxy-6-naphthoic acid (HNA) thermotropic random copolymers having different compositions and molecular weights. For rapidly cooled HBA-rich samples, the structure is pseudo-hexagonal, while for the more HNA-rich it is slightly distorted to orthorhombic, a phase designated O". On annealing, the HBA-rich samples undergo a partial phase transformation to a denser orthorhombic phase with a greater distortion from the hexagonal than the O". This new phase is designated O'. Annealing of the samples richer in HNA leads to a greater distortion of the O" cell away from hexagonal, but no increase in density. Discrete small-angle diffraction maxima corresponding to a long period of ~ 300 A appear only in those samples containing the denser O' phase, with the implication that both pseudo-hexagonal and O" crystals have densities very close to that of the non-crystalline nematic matrix. Anneals above 230°C lead to a marked increase in long period and there was some evidence of a specific doubling mechanism. Precise measurement of crystallinity gave values between 17.5% and 25.5%, the lower values being in the samples closer to the 1:1 composition and in those annealed

Детальніше...  

Корисні статті

Інженер-машинобудівник

Ні для кого не секрет, що при сучасних умовах життя, темпах розвитку промисловості, безперервній автоматизації та оптимізації роботи механізмів та виробничих процесів, великою популярністю та попитом на ринку праці користується професія інженера, особливо інженера-машинобудівника.

Щоб відповісти на питання «Хто такий інженер-машинобудівник?», необхідно розуміти , що несе в собі кожне з цих слів окремо. Інженер – це людина, яка отримала освіту з визначеного фаху. Інженер – це творець техніки. Інженер – це особа, що професійно займається інженерією, тобто на основі поєднання прикладних наукових знань, математики та винахідництва знаходить нові рішення технічних проблем. Тобто, виходячи з цих загальновживаних визначень слова «інженер» зрозуміло, що цій професії може присвятити себе лише людина з неабиякими здібностями, які ґрунтуються на знанні точних наук, логічному мисленні, невичерпному терпінні і постійному бажанні вдосконалювати світ інженерії. Від латини ingenium — здатність, винахідливість, що є свідченням того, що інженером перш за все є людина-думаюча, яка знаходиться в безперервному пошуку відповідей на складні технічні завдання.

Як стати інженером?

Кожна людина в процесі свідомого життя стикається з проблемою вибору професії. Найбільш актуальною ця проблема є для учнів старших класів – випускників, які добровільно або примусово здають шкільні іспити та зовнішнє незалежне оцінювання, за результатами чого приймають участь в конкурсному відборі на навчання у ВНЗ. Щоб обрана професія не стала важким випробовуванням, потрібно ще у шкільні роки зважити всі «за» і «проти», оцінити свої здібності, схильності, можливості.

Інженер-конструктор

Хто такий інженер-конструктор? Даним питанням задаються багато людей, які бажають пов'язати своє життя з цією професією. Варто відзначити, що ця професія однією з найбільш високооплачуваних на сучасному ринку праці, яка характеризується високим попитом з боку роботодавців. Інженер-конструктор машинобудування повинен володіти аналітичним складом розуму, підвищеною уважністю до деталей і відповідальним підходом до роботи. Дана діяльність пов'язана з прорахунками і різноманітним обладнанням. Першокласний інженер-конструктор механік володіє також такими рисами характеру, як раціональність і ерудованість. Важливу роль відіграє стресостійкість, адже робочий процес є досить трудомістким і при потребі замовника вимагає готовності швидко вносити зміни в готові креслення.

Рейтинг вищих навчальних закладів

На даний час в світі існує маса університетів з дуже великою кількістю кваліфікацій, спеціальностей та спеціалізацій. Одні з них більш престижні університети, інші менш.

Рейтинг вищих навчальних закладів переписується щорічно, в зв'язку з тим, що всі прагнуть стати краще в освіті, вдосконалитися в технологіях і підвищити свій рівень акредитації. Рейтинг навчальних закладів варіюється в залежності від предметної області, це природничі науки і математика, техніка/технологія і інформатика, життя і сільськогосподарська наука, клінічна медицина і фармація, соціальні науки.

Вибір професії

Кожна людина зіштовхується у своєму житті з вибором, який найсильніше вплине на все її подальше життя. Йдеться про вибір професії та вибір вищої освіти. Закінчуючи школу, молоді люди стикаються з величезним вибором професій та спеціальностей: інженер, економіст, юрист, менеджер, маркетолог, логіст, фінансист і т.д. При цьому навколо можна чути безліч стереотипних фраз: "Юристи багато заробляють", "Фінансисти працюють з грошима, тому у них хороші зарплати", "Маркетолог - основний людина в будь-якому бізнесі", а часом і просто без обґрунтування - "Менеджер - це круто ". Часом, такі "поради" впливають на вибір професії.