A polystyrene-polyethylene (PS-PE) interpenetrating polymer network (IPN)-like system was prepared by synthesis in situ. The system differs from 'pure' IPN systems in that the PS network is partially grafted onto the PE network. The mean molar mass of the polymer chain between two junction points (/~c) was calculated from the values of uniaxial compression modulus. Differential scanning calorimetry and thermomechanical analysis measurements pointed to a considerable decrease of the crystalline phase in PE with increasing PS content. The melting temperature enhancement of the crystalline phase of PE is discussed.
Raman microspectroscopy was used to follow the crystalline phase transformation produced when Knoop and Vickers microindentations are made in poly(vinylidene fluoride). An evolution of the degree of crystalline phase transformation was observed along the microindentations which can be schematized into three regions. A high gradient in the degree of crystalline transformation was detected near the centre of the indentation, whereas Raman microanalysis of the region near the edges of the impression did not indicate a significant variation in the crystalline phase modification. An explanation for these observations is proposed.
Light scattering measurements were made of glutaraldehyde (GA)-cured gelatin gels. Gel modulus, which was found by intensity measurements of scattered light, decreased with increasing GA content, and the autocorrelation function of dynamic light scattering could be reproduced by a double-exponential fitting. The diffusion constant of the fast mode was proportional to gelatin concentration, Ce, to the power of 0.79, while the correlation length of the slow mode hardly depended on Ce. These facts suggested that GA curing may not influence the size of crystalline triple-helical structure but depresses the number of nucleation sites, which leads to lowering of the total crosslink density. Further, chemical and/or physical crosslink densities of GA-cured gelatin gels were estimated roughly by using swelling ratio data.
Poly(p-phenylene benzobisthiazole) (PBZT) polymer film, prepared by a doctor-blading technique, was studied by wide-angle X-ray scattering. Emphasis was placed on the anisotropic arrangement of the extended rigid-rod chains against the macroscopic axes. Two X-ray patterns, one measured with the X-ray beam perpendicular to the plane of the film surface and the other with the beam parallel to the surface plane, revealed a unique morphological feature: the large molecular plane of the PBZT chain is lying perpendicular to the film surface plane with the long polymer axis being random but lying in the plane of the film surface.
The crystal structure of the syndiotactic polystyrene-toluene molecular compound was studied by X-ray diffraction. The crystal data are as follows: monoclinic system, space group P21/a (no. 14), a=17.58, b= 13.26, c(chain axis)=7.71 A, 7= 121.2 °, eight monomer units (two chains) and two toluene molecules per unit cell, the molar ratio of monomer: toluene being 4:1. The polymer chains take a twofold helical structure of (-TTGG-)2 conformation, and the packing of the polymer chains enables each toluene molecule to occupy an isolated hole between the benzene rings of adjacent polymer chains. The molecular compounds with benzene, chlorobenzene, p-xylene, 1,2,4-trichlorobenzene and so on are isomorphous to the toluene molecular compound. These molecular compounds are commonly transformed on heating between 120 and 150°C to another crystalline phase free from the guests, in which the polymer chains retain the helical structure.
Diblock polystyrene-block-poly(hydrogenated isoprene) was fluorescence labelled by random covalent attachment of anthracene at the polystyrene block (the average number of anthracenes per copolymer chain was 0.88). Micellization of the labelled copolymer was studied in a broad composition range of the solvent mixture 1,4-dioxane/heptane. Micelles with polystyrene cores are formed in heptane-rich solvents (0-30 vol% 1,4-dioxane). In mixtures with 30-50 vol% 1,4-dioxane, the sample dissolves molecularly in the form of individual copolymer coils and in dioxane-rich solvents (more than 50 vol% 1,4-dioxane), micelles with polystyrene shells are formed. Micellar solutions were characterized by static and quasielastic light scattering and by sedimentation velocity measurements. The mobility of pendant fluorophores and polymer segments in micellar cores and shells in selective solvents and in individual copolymer coils in good solvents was studied by time-resolved fluorescence-anisotropy measurements.
The effect of electron beam irradiation on the morphology and mechanical properties of biaxially drawn ultra-high molecular weight polyethylene dried gel films was investigated as a function of irradiation dose in terms of cross-linking and main-chain scission. Tensile strength and elongation decrease drastically, even with small irradiation doses, while the storage modulus increased with increasing dose up to 20 Mrad over a temperature range from 0 to 120°C. This indicates that electron beam irradiation causes cross-linking and main-chain scission; the former improves heat resistance and the latter causes deterioration of tensile strength.
Colourless polyoxadiazoles containing both hexafluoroisopropylidene and diphenylsilyl groups in the backbone have been synthesized. The new film-forming polymers are soluble in common solvents (tetrahydrofuran, CHC13) and are stable (by thermogravimetric analysis) to about 500°C in both nitrogen and air.
The crystal structure of a planar zigzag form of syndiotactic polystyrene (planar form I) obtained by annealing as-cast samples from solutions (molecular compounds with the solvents) was studied by X-rays. Crystal data are as follows: orthorhombic system, space group P212121 (no. 19), but finally Pbnm (no. 62), a = 8.81 ~,, b = 28.82 A, c (chain axis)= 5.06 ~, eight monomer units (four chains) per unit cell. Planar form I is different in alignment of the planar zigzag chains from planar form II obtained by melt-crystallization, which belongs to the hexagonal system. Moreover, the crystal structure of planar form I is characterized by a 'stacking fault' in the molecular packing
The miscibility of binary polymer blend systems consisting of poly(vinyl methyl ether) (PVME) and polyacrylates has been studied. Based on film clarity, glass transition temperature and cloud-point studies, PVME is found to be miscible with poly(ethyl acrylate), poly(n-propyl acrylate) and poly(n-butyl acrylate) but not with poly(methyl acrylate). The phase diagrams of some of these blends are reported.
Корисні статті
Рейтинг вищих навчальних закладів
На даний час в світі існує маса університетів з дуже великою кількістю кваліфікацій, спеціальностей та спеціалізацій. Одні з них більш престижні університети, інші менш.
Рейтинг вищих навчальних закладів переписується щорічно, в зв'язку з тим, що всі прагнуть стати краще в освіті, вдосконалитися в технологіях і підвищити свій рівень акредитації. Рейтинг навчальних закладів варіюється в залежності від предметної області, це природничі науки і математика, техніка/технологія і інформатика, життя і сільськогосподарська наука, клінічна медицина і фармація, соціальні науки.
Як стати інженером?
Кожна людина в процесі свідомого життя стикається з проблемою вибору професії. Найбільш актуальною ця проблема є для учнів старших класів – випускників, які добровільно або примусово здають шкільні іспити та зовнішнє незалежне оцінювання, за результатами чого приймають участь в конкурсному відборі на навчання у ВНЗ. Щоб обрана професія не стала важким випробовуванням, потрібно ще у шкільні роки зважити всі «за» і «проти», оцінити свої здібності, схильності, можливості.
Хімічне машинобудування
Хімічне машинобудування багатопрофільна галузь машинобудування, що поєднує в собі природні та експериментальні науки (наприклад, фізика і хімія), разом з науками про життя (наприклад, біологія, мікробіологія та біохімія). Математику та економіку вокористовують для розробки, перетворення, транспортування, управління виробничими процесами, які перетворюють сировину в цінні продукти.
Вибір професії
Кожна людина зіштовхується у своєму житті з вибором, який найсильніше вплине на все її подальше життя. Йдеться про вибір професії та вибір вищої освіти. Закінчуючи школу, молоді люди стикаються з величезним вибором професій та спеціальностей: інженер, економіст, юрист, менеджер, маркетолог, логіст, фінансист і т.д. При цьому навколо можна чути безліч стереотипних фраз: "Юристи багато заробляють", "Фінансисти працюють з грошима, тому у них хороші зарплати", "Маркетолог - основний людина в будь-якому бізнесі", а часом і просто без обґрунтування - "Менеджер - це круто ". Часом, такі "поради" впливають на вибір професії.
ВНЗ України
Вища освіта є невід'ємним елементом перспективного кар'єрного росту, тому перед кожним абітурієнтом виникає проблема, в які інститути подавати документи. Варто відзначити, що в Україні існує велика кількість вузів. Всі навчальні заклади поділяються на державні та приватні, пропонуючи різноманітні освітні програми по різних профілів. Щоб пошук інститутів дав задовільні результати, слід визначитися з найбільш прийнятними спеціальностями. Також підбір університету передбачає вибір підходящої форми навчання, наявність високої акредитації у вузу і рівень його престижності.