The influence of fibre diameter on the tensile strength of solution-spun, ultra-drawn, ultra-high molecular weight polyethylene (UHMW-PE, Mw > 103 kg mo1-1 ) fibres was investigated. Fibres with a wide range of diameters were produced by varying the polymer concentration in solution and by applying a drawdown to the fibres. The tensile strength of drawn fibres is compared at a constant Young's modulus in order to eliminate the influence of morphological parameters, such as degree of chain orientation and extension, on the fracture behaviour. It is shown that the tensile strength of UHMW-PE fibres is independent of the fibre diameter. In accordance with previous studies, it is found that fibre fracture is initiated by molecular events, such as chain scission.
A set of hydroxyl-terminated oligo(ether-ketones) based on isophthaloyl and oxyphenylene units were synthesized by conventional means involving Friedel-Crafts and Ullmann reactions. The pure dihydroxy intermediates were functionalized by end-capping with 3- and 4-ethynylbenzoylchloride. The synthetic route yielded oligomers of well defined composition, which could be readily confirmed by n.m.r. Solubility and thermal behaviour greatly depended on the ratio of m- to p-substituted phenylene rings present in the oligomers. All of the oligomers cured to insoluble, thermally stable materials after heating to 150-300°C and showed glass transition temperatures at ~250°C
The longitudinal Poisson's ratios vlt of the crystal lattice of poly(p-phenylene terephthalamide), namely Kevlar 49 and Kevlar 29, were evaluated by X-ray diffraction. Linear contraction of the crystal lattice in the direction perpendicular to the chain axis was observed up to 800 MPa. The v~t values for the (I 0 0), (0 1 0) and (1 1 0) planes are obtained as follows
The miscibility of poly(tetrahydropyranyl-2-methyl methacrylate) (PTHPMA) with poly(styrene-coacrylonitrile) (SAN) and poly(p-methylstyrene-co-acrylonitrile) (pMSAN) has been studied by differential scanning calorimetry. PTHPMA is miscible with SAN having an acrylonitrile (AN) content between 0 wt% and 31wt%, and with pMSAN having an AN content between 5wt% and 29wt%. Three segmental interaction parameters, ~(THPMA/S, THPMA/pMS and ~THPMA/AN, were found to be -0.011, 0.019 and 0.64, respectively.
The effect of copolymerization with propylene on the fracture behaviour of solution-spun ultra-drawn, ultra-high molecular weight polyethylene (UHMW-PE, M w > 103 kgmo1-1) fibres was investigated. UHMW-PE grades with virtually identical molecular weight and varying comonomer content (0.5-13.5 CH3/1000 C atoms) were used. It is shown that the tensile strength of drawn UHMW-PE fibres, at a constant Young's modulus, is independent of the comonomer content of the polymer. Apparently, the methyl side-groups hardly influence the fracture behaviour of the fibres. In combination with the experimental observation that methyl side-groups decrease intermolecular chain slippage (creep), this indicates that the failure process of solution-spun, drawn UHMW-PE fibres is mainly controlled by chain scission
Poly[ (R)-3-hydroxyalkanoate]s (PHAs) are bacterial storage polyesters, which are accumulated by a range of micro-organisms as intracellular granules. In contrast to the isolated PHA, the nascent polymer in the granules does not crystallize but remains amorphous at ambient temperature. A lot of studies have been devoted to this phenomenon and all claimed the in vivo presence of a highly effective plasticizer. In contrast, this paper demonstrates that the native granules do not contain a plasticizer and that the amorphous state of in vivo PHA can be explained simply by straightforward crystallization kinetics
The mechanical anisotropy of injection moulded plaques of a liquid crystalline polymer based on a copolyester of p-hydroxybenzoic acid, isophthalic acid and hydroquinone has been studied. The inhomogeneity of the elastic anisotropy has been determined by a combination of static and ultrasonic measurements. The elastic constants are discussed in the light of previous results for anisotropic polymers and are shown to be consistent with an aggregate model to describe the relationship between mechanical anisotropy and molecular orientation.
The miscibility behaviour of poly (cyclohexyl methacrylate ) (PCHMA) with poly (styrene-co-acrylonitrile) (SAN) and poly(p-methylstyrene-co-acrylonitrile) (pMSAN) was investigated by differential scanning calorimetry. PCHMA was found to be miscible with SAN having acryionitrile (AN) content up to 20 wt%, and with pMSAN having AN content up to 22 wt%. All miscible blends were examined for the lower critical solution temperature (LCST) behaviour and the results were used to construct the phase diagrams.
The effects of changing matrix ductility are studied for rubber-toughened epoxy resins with modification of the rubber/matrix interfacial zone. The interfacial modification results in a large and more deformable interfacial zone, which gives rise to a further increased fracture toughness. Various microstructural parameters and the deformation and fracture behaviours of the rubber-toughened epoxy resins are quantified. Epoxy resins with moderate ductility are more effective in increasing further toughness after modification of the rubber/matrix interfacial zone. The further increased toughness results solely from the increased cavitation that arises in the modified rubber/matrix interfacial zone. On the other hand, the size of the plastic deformation zone in the vicinity of the crack tip is independent of the degree of rubber cavitation, but it is significantly increased by multiple but localized shear yielding, caused by the increase in matrix ductility. In addition, the degree of multiple but localized shear yielding is independent of the degree of cavitation in the present investigation.
Poly[(R)-3-hydroxybutyrate] (PHB), a bacterial polyester, is subject to a detrimental ageing process, which hampers its application possibilities. This ageing phenomenon is usually studied using moulded specimens, and was found to be related to a loss in segmental mobility. The presence of additives and orientation in moulded PHB samples might influence this ageing process. As a reference for our ageing studies, we therefore conducted a study on the ageing effects in virgin PHB powder. For this purpose a method is required to measure the mobility in a powder without the employment of heat or mechanical strain, since these are known to induce deageing. This paper describes a suitable technique based on the principle that the variation of the radical concentration with temperature after y-irradiation at 77 K provides a measure of the changes in the segmental mobility of the polymer chains
Корисні статті
Рейтинг вищих навчальних закладів
На даний час в світі існує маса університетів з дуже великою кількістю кваліфікацій, спеціальностей та спеціалізацій. Одні з них більш престижні університети, інші менш.
Рейтинг вищих навчальних закладів переписується щорічно, в зв'язку з тим, що всі прагнуть стати краще в освіті, вдосконалитися в технологіях і підвищити свій рівень акредитації. Рейтинг навчальних закладів варіюється в залежності від предметної області, це природничі науки і математика, техніка/технологія і інформатика, життя і сільськогосподарська наука, клінічна медицина і фармація, соціальні науки.
Хімічне машинобудування
Хімічне машинобудування багатопрофільна галузь машинобудування, що поєднує в собі природні та експериментальні науки (наприклад, фізика і хімія), разом з науками про життя (наприклад, біологія, мікробіологія та біохімія). Математику та економіку вокористовують для розробки, перетворення, транспортування, управління виробничими процесами, які перетворюють сировину в цінні продукти.
Полімерні матеріали
Полімер це велика молекула, або макромолекула, котра складається з багатьох субодиниць. Через їх широкий спектр властивостей, синтетичні і природні полімери відіграють найважливішу і всюдисущу роль в повсякденному житті. Полімери в діапазоні від знайомих синтетичних пластмас, таких як полістирол природний біополімер, таких як ДНК і білки, які є основоположними для біологічної структури і функцій. Полімери, як природні і синтетичні, створюються за допомогою полімеризації багатьох малих молекул, відомих як мономери.
Комп'ютер для інженера
У сучасному світі комп'ютери дуже поширені. Складно уявити людину, не знайому з цим поняттям. Багато професій зобов'язані своїм виникненням саме комп'ютеру, вони б просто не з'явилися без створення електронно-обчислювальної техніки.
І хоча відносно недавно, на початку XX століття, комп'ютери були розкішшю і використовувалися лише для самих складних розрахунків, у наш час комп'ютери та комп'ютерна техніка дуже глибоко інтегрувалися у наше життя. Сучасне людство залежить від комп'ютерів, що викликає подиву, якщо розглянути, коли і в яких випадках вони використовуються.
Хто такий інженер
Інженер - професія нелегка, але одночасно з цим дуже цікава і захоплююча. Адже інженер це людина, у якого народжуються в голові нові ідеї і тому він здатний винаходити.
У багатьох виникає питання: хто такі інженери? Інженер (франц. Ingénieur) - фахівець з вищою технічною освітою. Спочатку інженерами називали людей, які керували військовими машинами. Поняття громадський інженер з'явилося в XVI столітті в Голландії, застосовано до сфери будівництва мостів і доріг, потім інженери з'явилися в Англії, а потім в інших країнах.