The compatibilizing effect of styrene-methyl methacrylate block copolymer (SM) on blends of poly(2,6-dimethyl-l,4-phenylene ether) (PPE) and poly(hydroxy ether of bisphenol A) (Phenoxy) was examined in terms of phase structure and rheological and mechanical properties. Scanning electron micrographs show that the blends exhibit a more regular and finer dispersion when a small amount of the SM block copolymer is added. The interfacial tension between two immiscible polymers in the blends is estimated by applying various theories of emulsion models to the results of theological measurements. The interfacial tension is significantly reduced when 5 wt % of the copolymer is added. Thermal analysis suggests that the added block copolymer is located at the interface of the PPE and Phenoxy. The blends exhibit remarkably enhanced toughness with the addition of a small amount of SM, which seems to be attributable to both dispersed particle size reduction and improved interfacial adhesion.

Детальніше...  

The dielectric and dynamic mechanical relaxation behaviours of the thermoplastic polyimide, NEW-TPI, have been investigated from 150 to 350°C, which spans the glass transition region. Dynamic modulus at 1 Hz is about 2.2 GPa below the glass transition temperature, T~, decreasing to 0.02 GPa in amorphous NEW-TPI, and 0.15 GPa in semicrystalline NEW-TPI, above Tg. Dielectric constant at 10kHz is about 3.21 below Tg, increasing to 3.44 in amorphous NEW-TPI, and 3.33 in semicrystalline NEW-TPI, above Tg. Williams-Landel-Ferry (WLF) plots for amorphous and one representative semicrystalline NEW-TPI were constructed from thermal, dynamic mechanical and dielectric relaxation data but the data could not be fitted to a single master curve. Dielectric relaxation intensity, Ae=es-~, was shown to be structure sensitive above T~. For both semicrystalline and amorphous NEW-TPI, the relaxation intensity decreases as temperature increases. This implies that Ae has the same temperature dependence for the semicrystalline sample compared to the quenched amorphous polymer. This trend is different from that observed in either poly(ether ether ketone) or poly(phenylene sulphide). Our results confirm thermal analysis of NEW-TPI and show that NEW-TPI has a very small amount of tightly bound, or rigid, amorphous material, which relaxes completely within a narrow temperature range just above the Tg of the less tightly bound, or mobile, amorphous material.

Детальніше...  

The vinylester resin around a silane-finished glass fibre was measured using a microscopic FTi.r. spectrometer. It is argued that the silane affected the curing process of the vinylester resin at a great distance compared to the thickness of the silane interphase.

Детальніше...  

Birefringence, infra-red dichroism and shrinkage-stress data of poly(aryl ether ether ketone) (PEEK) uniaxially drawn above the glass transition have been analysed in the framework of the theory of rubber elasticity. It is shown that PEEK chains having a molecular weight M,~13000 only contain three entanglements per chain on average. The very low level of shrinkage stress of the samples having a draw ratio below the threshold of strain-induced crystallization is perfectly consistent with a weakly entangled network. The birefringence versus stress curve discloses an orientation-dominated regime at low strains and a deformation-dominated regime starting from the onset of the strain-induced crystallization. The length of the random link, L= 1.8 nm, is in very good agreement with the one that can be theoretically predicted for the stiff-chain polymer relatives, poly(ethylene terephthalate), polycarbonate and poly(phenylene oxide). A value for the intrinsic birefringence of the amorphous phase, An~ = 0.38_ 0.04, is also reported

Детальніше...  

Poly(dipropargyl terephthalate), a high molecular weight linear soluble polymer, was prepared by the so-called oxidative polymerization by oxidation of the two terminal hydrogen atoms of dipropargyl terephthalate. The polymer undergoes easy thermal and radiation cross-linking via solid (crystalline) state topochemical polymerization of its two conjugated triple bonds (diacetylene linkages) of the main chain without changes in polymer crystalline lattice. This type of polymer appears attractive for preparation of (self-) cross-linkable thermosetting fibres.

Детальніше...  

The determination of average molar masses and molar mass distributions (MMDs) of polymers and polyelectrolytes is demonstrated with the new analytical ultracentrifuge Optima XL-A and its very sensitive digital u.v./vis, detector (180 800nm continuously) from Beckman Instruments, Inc. The machine was tested with the narrow distribution polystyrenes PS 106000 and 300000 (and a 50:50 mixture), sodium poly(styrene sulfonate) NaPSS 100000 and the broad distribution polystyrene NBS 706. Full details of the calculation of average molar masses and MMDs of the polymers from the experimental values are given. The results show that the new absorption optics enable the above-mentioned quantities to be determined as the absorption optics are able to measure at very low concentrations, which allows either a precise extrapolation to zero concentration or averaging of the data. Owing to the fact that a sedimentation run is a real fractionation process (with a higher resolution than size exclusion chromatography) one measures the real MMD. There is no need to presume a special model MMD to analyse the measurement data. The data from the Optima XL-A are accessible as ASCII-files. As the original Beckman computer programs are not suitable for our purposes, we have developed own programs, which are available on request

Детальніше...  

Extrusion of poly(ethylene terephthalate)/poly(ethylene 2,6-naphthalene dicarboxylate) blends results in transesterification reactions between the two polymers. In this study, the effects of blending time, temperature, blend composition and polyester catalyst on transesterification were determined using nuclear magnetic resonance, and rate constants and an activation energy for the process were determined. Over the ranges studied, the primary factors controlling the transesterification were the blending time and temperature, while the composition of the blend and the residual polyester catalysts had little or no effect on the interchange reactions. In addition, differential scanning calorimetry measurements demonstrated that transesterification led to the formation of a single amorphous phase

Детальніше...  

This paper is concerned with the existence of partial miscibility of a polyetherimide (PEI) with both amorphous and semicrystalline liquid crystalline polymers (LCPs) and its effect on the morphology of the blends of these polymers. Partial miscibility was determined by measuring the shift in the glass transition temperatures as determined by dynamic mechanical thermal analysis and differential scanning calorimetry. With increasing concentration of the LCP in the PEI/LCP blends, the glass transition temperature of the PEI phase shifted to a lower temperature. Annealing and mixing history were also observed to affect the degree of shift in the glass transition temperature. Morphologies of the partially miscible systems were found to be quite different from those of an immiscible system. It is likely that due to partial miscibility in these blends, a PEI-LCP solid solution coexists with the neat LCP phase

Детальніше...  

The preparation of a series of hydrogel copolymer membranes of 2-hydroxyethyl methacrylate with 4-vinyl pyridine (VPy) in the range of0.5-17 wt%, or 4'-vinyl 4-methyl 2,2'-bipyridine (VBpy) in the range 0.5-8 wt%, are described. The membranes are shown to coordinate selected transition metal ions from aqueous solution. Interactions with Cu(n) and Fe(ii) were isolated for individual attention on the basis that, under certain conditions, bands appear in the visible spectra characteristic of the Cu(u) tetra(VPy) and the Fe(n) tris(VBpy) complexes. The complexation of more than one ligand group per metal ion leads to the potential anchoring of two or more previously unconnected polymer chains at a metal-centred cross-link. The effects of 'coordinative cross-linking' on the tensile properties of the hydrogel polymers were studied in elongation at 25°C and 100% humidity, until failure of the membranes occurred. The tensile strengths of both the Cu(n) and Fe01)-coordinated polymers are found to increase in conjunction with copolymer ligand content, as a consequence of a greater degree of coordinative cross-linking. In more classical hydrogel systems, the equilibrium water content of the polymer is caused to fall with degree of cross-linking. Here, this is not the case, as the equilibrium water content remains relatively unchanged owing to the incorporation of further water-structuring groups in the guise of metal complexes. Together with the capability of a reversible crossqinking effect by metal leaching under acid conditions, these ligand-modified systems offer a novel and unique route to the enhancement of mechanical properties in hydrogel-type materials.

Детальніше...  

The influence of injection-moulding conditions on the anisotropy in macroscopic properties of flat rectangular plates has been evaluated for a thermotropic main-chain liquid crystalline polymer. The anisotropic mechanical and thermal behaviour is correlated to the degree of molecular ordering as determined from X-ray diffraction. The geometry of the injection-moulded plates, such as their thickness and the thickness and shape of the sprue, as well as the injection speed, significantly affect the molecular ordering and the resulting anisotropy in, for example, Young's modulus and heat conduction. The tendencies observed are explained in terms of molecular alignment as a consequence of the combination of shear, elongational fountain flow and the elongational deformation in the sprue.

Детальніше...  

Корисні статті

Інженер-механік

Інженер-механік (від лат. Ingenium – талант, обдарованість, і mēchanicus – механік) – це технічний чи технологічний фахівець з вищою освітою, який застосовує отримані знання для конструювання, проектування, моделювання та експлуатації машин, апаратів та технічного обладнання в різних галузях сільського господарства та технічного виробництва. Першими з інженерів були саме механіки; вони розробляли і збирали різноманітні машини і механізми, в яких використовували принципи і закони механіки.

Хімічне машинобудування

Хімічне машинобудування багатопрофільна галузь машинобудування, що поєднує в собі природні та експериментальні науки (наприклад, фізика і хімія), разом з науками про життя (наприклад, біологія, мікробіологія та біохімія). Математику та економіку вокористовують для розробки, перетворення, транспортування, управління виробничими процесами, які перетворюють сировину в цінні продукти.

Інженер-машинобудівник

Ні для кого не секрет, що при сучасних умовах життя, темпах розвитку промисловості, безперервній автоматизації та оптимізації роботи механізмів та виробничих процесів, великою популярністю та попитом на ринку праці користується професія інженера, особливо інженера-машинобудівника.

Щоб відповісти на питання «Хто такий інженер-машинобудівник?», необхідно розуміти , що несе в собі кожне з цих слів окремо. Інженер – це людина, яка отримала освіту з визначеного фаху. Інженер – це творець техніки. Інженер – це особа, що професійно займається інженерією, тобто на основі поєднання прикладних наукових знань, математики та винахідництва знаходить нові рішення технічних проблем. Тобто, виходячи з цих загальновживаних визначень слова «інженер» зрозуміло, що цій професії може присвятити себе лише людина з неабиякими здібностями, які ґрунтуються на знанні точних наук, логічному мисленні, невичерпному терпінні і постійному бажанні вдосконалювати світ інженерії. Від латини ingenium — здатність, винахідливість, що є свідченням того, що інженером перш за все є людина-думаюча, яка знаходиться в безперервному пошуку відповідей на складні технічні завдання.

Полімерні матеріали

Полімер це велика молекула, або макромолекула, котра складається з багатьох субодиниць. Через їх широкий спектр властивостей, синтетичні і природні полімери відіграють найважливішу і всюдисущу роль в повсякденному житті. Полімери в діапазоні від знайомих синтетичних пластмас, таких як полістирол природний біополімер, таких як ДНК і білки, які є основоположними для біологічної структури і функцій. Полімери, як природні і синтетичні, створюються за допомогою полімеризації багатьох малих молекул, відомих як мономери.

Як стати інженером?

Кожна людина в процесі свідомого життя стикається з проблемою вибору професії. Найбільш актуальною ця проблема є для учнів старших класів – випускників, які добровільно або примусово здають шкільні іспити та зовнішнє незалежне оцінювання, за результатами чого приймають участь в конкурсному відборі на навчання у ВНЗ. Щоб обрана професія не стала важким випробовуванням, потрібно ще у шкільні роки зважити всі «за» і «проти», оцінити свої здібності, схильності, можливості.